Abstract Lignin is an aromatic‐rich biomass polymer that is cheap, abundant, and sustainable. However, its application in the solid electrolyte field is rare due to challenges in well‐defined polymer synthesis. Herein, the synthesis of lignin‐graft‐poly(ethylene glycol) (PEG) and its conductivity test for a solid electrolyte application are demonstrated. The main steps of synthesis include functionalization of natural lignin's hydroxyl to alkene, followed by graft‐copolymerization of PEG thiol to the lignin via photoredox thiol‐ene reaction. Two lignin‐graft‐PEGs are prepared having 22 wt% lignin (lignin‐graft‐PEG 550) and 34 wt% lignin (lignin‐graft‐PEG 2000). Then, new polymer electrolytes for conductivity tests are prepared via addition of lithium bis‐trifluoromethanesulfonimide. The polymer graft electrolytes exhibit ionic conductivity up to 1.4 × 10⁻⁴ S cm⁻¹ at 35 °C. The presence of lignin moderately impacts conductivity at elevated temperature compared to homopolymer PEG. Furthermore, the ionic conductivity of lignin‐graft‐PEG at ambient temperature is significantly higher than homopolymer PEG precedents. 

Abstract Single‐ion conducting polymer electrolytes are of interest for use with advanced battery electrodes such as lithium metal, but achieving sufficiently high conductivity has been challenging. In this work, a model system containing charged sites that are precisely spaced along the polymer backbone is explored. Precision sulfonated poly(4‐phenylcyclopentene) lithium salt (p5PhS‐Li) with a high degree of sulfonation (> 90%) is synthesized and blended with poly(ethylene oxide) (PEO) to investigate the thermodynamic and transport properties. Melting point depression is measured via differential scanning calorimetry, ionic conductivity,κ, is determined using electrochemical impedance spectroscopy, and the fraction of current carried by Li⁺is estimated based on steady‐state current measurements. In conjunction with a density measurement, melting point depression is used to find an effective Flory–Huggins interaction parameter,χ_eff=   − 0.21, suggesting miscibility of the blend.κspans a large range from 2 × 10⁻¹¹to 2 × 10⁻⁷S cm⁻¹over the composition and temperature range investigated. The fraction of charge carried by lithium ions also spans a significant range from 0.12 in majority PEO blend to 0.98 in majorityp5PhS‐Li blend. This study addresses several limitations of sulfonated polystyrene and opens up the possibility of precisely controlling the spacing of other anion types.